Sabic LLDPE is a well-known LLDPE brand in the world. Sabic has researched and produced various specifications of LLDPE, including film grade, injection molding grade, extrusion applications, pipeline applications, wire and cable applications, etc.
Chemate, a leading and professional supplier of plastic materials with rich export experience, can provide customers with various models of Sabic LLDPE, including LLDPE 218WJ, LLDPE 118WJ, LLDPE 218BJ, LLDPE 118NJ, LLDPE 318BJ, LLDPE 219ZJ, etc. Feel free to tell us the models or grades you need, we will quote you the most competitive price quickly.
LLDPE 118NJ is TNPP free, does not contain slip and antiblock additives, and is generally used for general purposes. Films produced with this resin are tough, with good puncture resistance, high tensile strength and good hot tack.
SABIC® LLDPE 118NJ Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| OPTICAL PROPERTIES | ||
| Haze | 13 | % |
| Gloss (45°) | 50 | ‰ |
| FILM PROPERTIES | ||
| Tear strength MD | 40 | kN/m |
| Tensile test film | ||
| Modulus of elasticity MD | 160 | MPa |
| Stress at break TD | 30 | MPa |
| Strain at break MD | 700 | % |
| Strain at break TD | 850 | % |
| Stress at break MD | 37 | MPa |
| Modulus of elasticity TD | 180 | MPa |
| Yield stress TD | 11 | MPa |
| Tear strength TD | 120 | kN/m |
| Impact strength | 22 | kJ/m |
| POLYMER PROPERTIES | ||
| Density | 918 | kg/m³ |
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 1.0 | dg/min |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 100 | °C |
| DSC test | ||
| melting point | 121 | °C |
LLDPE 118WJ is commonly used for general purposes and is a kind of butene linear low density polyethylene resin. It is TNPP free, but contains slip and antiblocking agents. Films produced with Sabic 118wj are tough, with good puncture resistance, high tensile strength and good hot tack.
SABIC® LLDPE 118WJ Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| OPTICAL PROPERTIES | ||
| Gloss (45°) | 42 | ‰ |
| Haze | 20 | % |
| FILM PROPERTIES | ||
| Impact strength | 22 | kJ/m |
| Tear strength TD | 120 | kN/m |
| Tear strength MD | 40 | kN/m |
| Tensile test film | ||
| Strain at break TD | 800 | % |
| Strain at break MD | 600 | % |
| Modulus of elasticity MD | 160 | MPa |
| Modulus of elasticity TD | 180 | MPa |
| Stress at break TD | 30 | MPa |
| Yield stress TD | 11 | MPa |
| Stress at break MD | 37 | MPa |
| Coefficient of friction | 0.1 | – |
| Blocking | 15 | g |
| Re-blocking | 10 | g |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 1.0 | dg/min |
| Density | 918 | kg/m³ |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 101 | °C |
| DSC test | ||
| melting point | 121 | °C |
With additive, without TNPP, 218BJ is a food grade LLDPE, which can be widely used in food packaging , such as lamination film and barrier film. Meanwhile, it can also be used in industrial packaging and as a blending partner with other PE resins in blown and cast film applications. It has good thermal stability, allowing the resin to be used under critical extrusion processing conditions.
SABIC® LLDPE 218BJ Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| OPTICAL PROPERTIES | ||
| Gloss (45°) | 92 | ‰ |
| Haze | 1.2 | % |
| FILM PROPERTIES | ||
| Dart impact | 2.8 | kJ/m |
| Tear strength TD | 185 | kN/m |
| Protrusion Puncture resistance | 2.2 | J |
| Elastic recovery & Stress retention | ||
| Elastic recovery | 52.6 | % |
| Stress retention | 80 | % |
| Peel cling | ||
| 0% pre-stretch | 0.06 | N/mm |
| 200% pre-stretch | 0.05 | N/mm |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 2.0 | dg/min |
| Density | 918 | kg/m³ |
| DSC | ||
| melting point | 122 | °C |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at break | 17 | MPa |
| stress at yield | 12 | MPa |
| strain at yield | 16 | % |
| strain at break | 790 | % |
| Flexural test | ||
| Secant modulus at 1% elongation | 254 | MPa |
| Hardness Shore D | 48 | – |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 96 | °C |
| HIGHLIGHT PROPERTIES | ||
| Ultimate pre-stretch level | 310 | % |
| Retention force at 60 sec | 0.97 | kg |
| ELECTRICAL PROPERTIES | ||
| Volume resistivity | 5.0E15 | Ω.cm |
| Dissipation factor at 60 Hz | 1.0E3 | – |
| Dielectric constant at 60 Hz | 2.17 | – |
| Dielectric strength at 500 V/sec | 55 | V/µm |
218WJ is a kind of butene-free TNPP grade linear low density polyethylene, which is suitable for general purpose packaging. It contains slip and anti-blocking additives, has the advantages of easy processing, good tensile properties, impact strength and optical properties.
SABIC® LLDPE 218WJ Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| OPTICAL PROPERTIES | ||
| Haze | 13 | % |
| Gloss | ||
| at 60° | 80 | – |
| FILM PROPERTIES | ||
| Tensile Properties | ||
| stress at break, MD | 35 | MPa |
| stress at break, TD | 29 | MPa |
| strain at break, MD | 700 | % |
| strain at break, TD | 750 | % |
| stress at yield, MD | 12 | MPa |
| stress at yield, TD | 10 | MPa |
| 1% secant modulus, MD | 220 | MPa |
| 1% secant modulus, TD | 260 | MPa |
| Elmendorf Tear Strength | ||
| MD | 130 | g |
| TD | 320 | g |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190°C and 2.16 kg | 2 | g/10 min |
| Density | 918 | kg/m³ |
| FORMULATION | ||
| Slip agent | ☑ | – |
| Anti block agent | ☑ | – |
| MECHANICAL PROPERTIES | ||
| Dart Impact Strength | 85 | g/µm |
| THERMAL PROPERTIES | ||
| Vicat Softening Point | 98 | °C |
Sabic LLDPE 219ZJ is usually for general use. It is produced using solution technology. Films produced with this resin are tough, with good puncture resistance, high tensile strength and good hot tack.
SABIC® LLDPE 219ZJ Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| OPTICAL PROPERTIES | ||
| Gloss | ||
| Gloss (45°) | 50 | – |
| Haze | 13 | % |
| FILM PROPERTIES | ||
| Dart Impact Strength | ||
| Dart Drop Impact | 144 | g |
| Elmendorf Tear Strength | ||
| Tear Strength, MD | 220 | g |
| Tear Strength, TD | 318 | g |
| Tensile test film | ||
| 2% secant modulus, MD | 150 | MPa |
| 2% secant modulus, TD | 145 | MPa |
| Stress @ Yield, MD | 11.1 | MPa |
| Stress @ Yield, TD | 12.9 | MPa |
| Stress @ Break, MD | 29.5 | MPa |
| Stress @ Break, TD | 22 | MPa |
| Strain @ Break, MD | 950 | % |
| Strain @ Break, TD | 1130 | % |
| POLYMER PROPERTIES | ||
| Density | ||
| Density | 0.918 | g/cm³ |
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 2.0 | g/10 min |
318BJ is a kind of LLDPE model designed for ease of processing. It has been specifically formulated for optimum high temperature thermal stability during cast film extrusion process. Cast films produced from SABIC LLDPE 318BJ have excellent optical properties, puncture resistance and tear strength.
SABIC® LLDPE 318BJ Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at break | 13 | MPa |
| strain at yield | 16 | % |
| stress at yield | 12 | MPa |
| strain at break | 710 | % |
| Flexural test | ||
| Secant modulus at 1% elongation | 251 | MPa |
| Hardness Shore D | 48 | – |
| OPTICAL PROPERTIES | ||
| Gloss (45°) | 91 | ‰ |
| Haze | 2.1 | % |
| FILM PROPERTIES | ||
| Dart impact | 2.6 | kJ/m |
| Tear strength TD | 140 | kN/m |
| Protrusion Puncture resistance | 2.0 | J |
| Elastic recovery & Stress retention | ||
| Elastic recovery | 51.9 | % |
| Stress retention | 78.1 | % |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 2.8 | dg/min |
| Density | 918 | kg/m³ |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 102 | °C |
| DSC test | ||
| melting point | 121 | °C |
| ELECTRICAL PROPERTIES | ||
| Volume resistivity | 8.5E15 | Ω.cm |
| Dissipation factor at 60 Hz | 5.0E-4 | – |
| Dielectric constant at 60 Hz | 2.2 | – |
| Dielectric strength at 2000 V/sec | >30 | V/µm |
LLDPE M200024 is a injection molding grade linear low density polyethylene copolymer with a narrow molecular weight distribution. It has good low temperature toughness, stress crack resistance and gloss.
SABIC® LLDPE M200024 Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 20 | dg/min |
| Density | 924 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at yield | 12 | MPa |
| secant modulus at 1% elongation | 315 | MPa |
| strain at break | 450 | % |
| stress at break | 8.5 | MPa |
| Izod impact notched at 23 °C | 540 | J/m |
| Hardness Shore D | 55 | – |
| ESCR (100% Igepal CO-630), F50 | 24 | h |
| THERMAL PROPERTIES | ||
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 94 | °C |
| Brittleness Temperature | <-75 | °C |
Sabic LLDPE M500026 has a narrow molecular weight distribution and is suitable for injection molding applications. It has excellent flow properties, better low temperature toughness, stress crack resistance and gloss.
SABIC® LLDPE M500026 Technical Data Sheet
| PROPERTIES | TYPICAL VALUES | UNITS |
| POLYMER PROPERTIES | ||
| Melt Flow Rate (MFR) | ||
| at 190 °C and 2.16 kg | 50 | g/10 min |
| Density | 926 | kg/m³ |
| MECHANICAL PROPERTIES | ||
| Tensile test | ||
| stress at break | 12.4 | MPa |
| stress at yield | 13 | MPa |
| secant modulus at 1% elongation | 354 | MPa |
| strain at break | 120 | % |
| Izod impact notched at 23 °C | 450 | J/m |
| Hardness Shore D | 55 | – |
| ESCR (100% Igepal CO-630), F50 | 2 | h |
| THERMAL PROPERTIES | ||
| Brittleness Temperature | <-75 | °C |
| Vicat Softening Temperature | ||
| at 10 N (VST/A) | 88 | °C |
| LLDPE | Grades |
| Film Grade | 118LJ, 118NE, 118NJ, 118NJA, 118NM, 118WJ, 118WJA, 118WM , 118WSJ, 118ZJ, 119NJ, 119ZJ , 120NT, 120WJ, 121WJ, 122NJ , 122WJ, 128CNJ, 218B, 218BE, 218BJ, 218NF, 218NJ, 218NJA, 218NT, 218WJ, 218WJA, 218WM, 219NJ, 219ZJ, 220HT, 220NT, 220WT, 221WT, 222NJ, 222WF, 222WJ, 222WT, 318BE, 318BJ, 318BJA, 319BJ, 320BJ, 518NJ, 518NT, 6118LE, 6118NSF, 6135NE, 6318BE, 6318BJ, 6335BE, 6821NE, 6821NJ, 726NE, 920NT, 926NT, BX202, C2820T |
| Injection molding | M13024T, M200024, M200024T, M300024, M500026, M500026T, M50022T, MG200024, MG500026 |
| Extrusion applications | P438J |
| Pipeline applications | P1600A, R40039E, R50035, R50035E, R50035EE, RG50035 |
Sabic LLDPE price varies from model to model. Meanwhile, the purchase quantity is also one of the factors that affect the price. Welcome to contact us to get the latest quotation.