S-1300 PVC resin is mainly used in wire and cable, electrical insulating materials, cable sheathing, high-strength film products, artificial leather, soft boards and sheets, all-plastic sandals, auto parts, electrical appliances, as well as thermoplastic elastomers. Because Sinopec PVC resin S-1300 has higher viscosity than the general S-1000 PVC resin, its processing technology and mixing ratio are different. The properties of transparent sheets and salt films prepared with polyvinyl chloride resin S-1300 meet the requirements of relevant indicators. We can supply Sinopec S-1300 PVC resin produced by suspension method. Feel free to inquiry us for quotation now.
Application in cable material. The molecular weight distribution of PVC resin are to be more suitable for the needs of high-end cables. The mechanical properties of the cable material produced by S-1300 are better. Although the dielectric strength of S-1300 is slightly lower, it is still greater than the index requirements of insulating cable materials. So it will not affect its use in insulating materials.
Application in transparent flexible board. There are a wide variety of PVC soft boards on the market, such as door curtains, tablecloths, rain strips for car doors and windows, etc. The transparent soft board produced bu S-1300 has smooth surface, good transparency, no pitting, and fewer crystal points. The light transmittance, haze and yellow index of S-1300 transparent flexible board are better than the enterprise index, and it has better mechanical properties.
Application in thin films. PVC film products can be subdivided into agricultural film, calendered film and heat shrinkable film. Among them, heat shrinkable film is mainly produced with S-1000 type PVC, while agricultural film and calendered film are mainly produced with S-1300 PVC resin. The calendered film made of S-1300 and DOP plasticizer has the characteristics of high mechanical strength, good toughness, alkali resistance and exposure resistance, so its service life is more than 3 years.
In recent years, the output of PVC resin has increased rapidly, and the demand has also increased greatly. PVC resin gradually develops from generalization to high performance, specialization and engineering. With the maturity of PVC synthesis technology and the continuous improvement of PVC processing technology, both the PVC resin quality and the quality of PVC processing equipment, molds and products have been greatly improved. The wide use of compounding type parallel twin-screw extruders, two-stage extruders, reciprocating extruders and star-shaped mixing extruders in the PVC processing industry has created favorable conditions for the development of PVC from generalization to high performance and specialization.
Taking the production of cable materials as an example. In order to improve product performance, most cable material manufacturers have replaced the original S-1000 PVC resin with PVC resin S-1300 with higher degree of polymerization. And even some manufacturers have begun to use 1700 type or even 2500 type polyvinyl chloride resin with much higher degree of polymerization to produce high-grade cable material with much higher performance.