| Property | ISO Test Method | Test Condition | Unit | PA-777B Value |
| Melt Flow Index | 1133 | 220°C × 10kg | ml/10 min | 8.5 |
| Mass Density | 1183 | 23°C | g/cm³ | 1.03 |
| Tensile Strength (Yield) | 527 | 50 mm/min | MPa | 44 |
| Tensile Strength (Break) | 527 | 50 mm/min | MPa | 34 |
| Tensile Elongation | 527 | 50 mm/min | % | 40 |
| Flexural Strength | 178 | 2 mm/min | MPa | 67 |
| Flexural Modulus | 178 | 2 mm/min | GPa | 2.2 |
| Izod Impact Strength | 180/1A | 23°C Notched | kJ/m² | 21 |
| | | -30°C Notched | kJ/m² | 11 |
| Charpy Impact Strength | 179 | 23°C Notched | kJ/m² | 22 |
| | | -30°C Notched | kJ/m² | 11 |
| Vicat Softening Temperature | 306 | 1 kg, 50°C/hr | °C | 114 |
| | | 5 kg, 50°C/hr | °C | 106 |
| Heat Distortion Temperature | 75/A | 1.8 MPa Unannealed | °C | 86 |
| | | 1.8 MPa Annealed | °C | 106 |
| Thermal Expansion Coefficient | 11359 | – | 1/°C | 8.4 × 10⁻⁵ |
| Flammability | – | UL-94 | – | 1.5 mm HB |
| Mold Shrinkage | 294-4 | – | % | 0.3 – 0.6 |
| Symbol | 1043 | – | – | >ABS< |