| Property Category | Test Parameter | ISO Method | Test Conditions | Unit | PA-765B Value |
| Flow Properties | Melt Flow Index | 1133 | 220°C×10KG | g/10min | 44 |
| Physical Properties | Density | 1183 | 23°C | g/cm³ | 1.16 |
| Mechanical Properties | Tensile Strength (Yield) | 527 | 50 mm/min | MPa | 39 |
| | Tensile Strength (Break) | 527 | 50 mm/min | MPa | 30 |
| | Elongation at Break | 527 | 50 mm/min | % | 15 |
| | Flexural Strength | 178 | 2 mm/min | MPa | 57 |
| | Flexural Modulus | 178 | 2 mm/min | GPa | 1.8 |
| Impact Resistance | Izod Impact (23°C Notched) | 180/1A | 23°C | kJ/m² | 24 |
| | Izod Impact (-30°C Notched) | 180/1A | -30°C | kJ/m² | 11 |
| | Charpy Impact (23°C Notched) | 179 | 23°C | kJ/m² | 25 |
| | Charpy Impact (-30°C Notched) | 179 | -30°C | kJ/m² | 11 |
| Thermal Properties | Vicat Softening (A50) | 306 | 50°C/hr, 10N | °C | 94 |
| | Vicat Softening (A120) | 306 | 50°C/hr, 49N | °C | 80 |
| | HDT (1.8MPa Unannealed) | 75/A | 1.8 MPa | °C | 77 |
| | HDT (1.8MPa Annealed) | 75/A | 1.8 MPa | °C | 85 |
| | CTE | 11359 | – | 10⁻⁵/°C | 8.55 |
| Flammability | UL94 Rating | – | | | |
| | • 1.5mm thickness | – | – | – | V-2 |
| | • 2.5mm thickness | – | – | – | V-0 |
| | • 2.5mm thickness | – | – | – | 5VB |
| | • 3.0mm thickness | – | – | – | 5VA |
| Processing | Mold Shrinkage | 294-4 | – | % | 0.3-0.6 |
| Material Identification | ISO Code | 1043 | – | – | >ABS-FR(17)< |