Lotrene HDPE 5502 is specifically designed for the manufacture of blow molded packaging for household, industrial and cosmetics liquids.
| Physical Properties | Unit | Value |
| Density (23°C) | g/cm³ | 0.954 |
| Melt Index | dg/min | |
| 21.6 kg | 20 | |
| 2.16 kg | 0.2 | |
| Vicat Softening Point | °C | 127 |
| ESCR (100 % ant.) | h | 55 |
| Tensile Strength | MPa | |
| at yield (50 mm/min) | 27 | |
| at break (50 mm/min) | 31 | |
| Elongation | % | |
| at yield (50 mm/min) | 9 | |
| at break (50 mm/min) | min 700 | |
| Flexural Modulus | MPa | 1300 |
| Notched Tensile Impact Resistance | kJ/m² | |
| 23°C | 140 | |
| – 30°C | 115 |
HDPE 5502BN is tailored for lightweight blow molded containers that require excellent stiffness, exceptional processability, exceptional stress cracking resistance.
| Physical Properties | Unit | Value |
| Density | g/cm3 | 0.955 |
| Melt Index, Condition 190 C°/ 2.16 kgs | g/10min | 0.35 |
| HLMI, Condition 190 C°/21.6 kgs | g/10min | 33 |
| ESCR | ||
| Condition B, F50 (100% Igepal) | h | 24 |
| Tensile Yield Strength, 50 mm/ min | MPa | 27 |
| Elongation at Break, 50 mm/ min | % | >600 |
| Brittleness Temperature | °C | <-75 |
| Flexural Modulus, Tangent | MPa | 1370 |
| Shore D Hardness | – | 63 |
HDPE 50100 is tailored for large blow molded and thermoformed parts that. It has good melt strength, good rigidity, excellent ESCR, excellent low temperature impact strength.
| Physical Properties | Unit | Value |
| Density | g/cm3 | 0.948 |
| Melt Index, Condition 190 C°/ 2.16 kgs | g/10min | 0.06 |
| HLMI, Condition 190 C°/21.6 kgs | g/10min | 10 |
| ESCR | ||
| Condition B, F50 (100% Igepal) | h | >1000 |
| Tensile Yield Strength, 50 mm/ min | MPa | 26 |
| Elongation at Break, 50 mm/ min | % | >600 |
| Brittleness Temperature | °C | <-75 |
| Flexural Modulus, Tangent | MPa | 1170 |
| Shore D Hardness | – | 62 |
TR 144 is designed for film applications. It has good processability, good toughness and durability, good blending characteristics with HDPE HMW film resin.
| Physical Properties | Unit | Value |
| Density | g/cm3 | 0.946 |
| Melt Index, Condition 190 C°/ 2.16 kgs | g/10min | 0.18 |
| HLMI, Condition 190 C°/21.6 kgs | g/10min | 15 |
| Flexural Modulus, Tangent | MPa | 1150 |
| Brittleness Temperature | °C | <-75 |
| Typical Film Properties** | ||
| Dart Drop (66cm) | g | 90 |
| Spencer Impact Strength | J | 0.35 |
| Tensile Yield Strength, 50 mm/min | MPa | MD: 24 |
| TD: 26 | ||
| Elongation at Break, 50 mm/min | % | MD: 480 |
| TD: 640 | ||
| Elmendorf Tear Strength | g | MD: 19 |
| TD: 270 |